The lifetime of articulating surfaces in joint endoprostheses made of ultra-high molecular weight polyethylene (UHMW-PE), especially of UHMW-PE-cups of hip-endoprostheses, is usually limited to 10-15 years due to material failure as a result of oxidation of the UHMW-PE in vivo. In this study the suitability of the natural antioxidant alpha-tocopherol (vitamin E) as a stabilizer for UHMW-PE in these applications was investigated. Specimens with 0.1%, 0.2%, 0.4% and 0.8% w/w alpha-tocopherol as well as unstabilized samples were sintered and sterilized with gamma-rays at 25 kGy in accordance with standard processing methods of cups for total hip-endoprostheses. These specimens were aged in pure oxygen at 70 degrees C and 5 bar as well as in aqueous H2O2 at 50 degrees C. The degree of oxidation was observed by means of FTIR-spectroscopy, DSC analysis and mechanical testing. The FTIR-measurements showed that alpha-tocopherol can prolong the lifetime of UHMW-PE in an oxidative environment by a factor of more than 2.5. In the mechanical tests no embrittlement could be observed with the stabilized samples. A comparison with the standard antioxidant system Irganox 1010/Irgafos 168 (Ciba-Geigy, Switzerland) was carried out and revealed that alpha-tocopherol can even exceed the stabilization effect of this widely-used antioxidant system.