Magnesium alloys are promising materials for biomedical applications because of many outstanding properties like biodegradation, bioactivity and their specific density and Young's modulus are closer to bone than the commonly used metallic implant materials. Unfortunately their fatigue properties and low corrosion resistance negatively influenced their application possibilities in the field of biomedicine. These problems could be diminished through appropriate surface treatments. This study evaluates the influence of a surface pre-treatment by shot peening and shot peening+coating on the corrosion properties of magnesium alloy AZ31. The dicalcium phosphate dihydrate coating (DCPD) was electrochemically deposited in a solution containing 0.1M Ca(NO3)2, 0.06M NH4H2PO4 and 10mL/L of H2O2. The effect of shot peening on the surface properties of magnesium alloy was evaluated by microhardness and surface roughness measurements. The influence of the shot peening and dicalcium phosphate dihydrate layer on the electrochemical characteristics of AZ31 magnesium alloy was evaluated by potentiodynamic measurements and electrochemical impedance spectroscopy in 0.9% NaCl solution at a temperature of 22±1°C. The obtained results were analyzed by the Tafel-extrapolation method and equivalent circuit method. The results showed that the application of shot peening process followed by DCPD coating improves the properties of the AZ31 surface from corrosion and mechanical point of view.
Keywords: Coating; Corrosion; Electrochemical impedance spectroscopy; Mg-alloy; Shot peening.
Copyright © 2014 Elsevier B.V. All rights reserved.