The influence of fiber Bragg grating diameter when measuring strain is investigated and quantified. Two fiber Bragg gratings with bare cladding diameter of 125 μm and 80 μm are produced by excimer laser irradiation through a phase mask, and are used to simultaneously monitor the Bragg wavelength shift due to the strain produced by the solidification of a photo-curable resin during light exposure. It is found that the ratio of the measured strains in the two fiber Bragg gratings is close to the inverse ratio of the fiber's cladding diameter. These results represent a direct simultaneous comparison between 125 μm and 80 μm diameter fiber Bragg grating strain sensors, and demonstrate the feasibility of strain measurements in photo-curable resins using bare 80 μm cladding diameter fiber Bragg gratings with an increased sensitivity and spatial resolution compared with standard 125 μm diameter fiber Bragg gratings.