Characterization and Microstructural Evolution of Continuous BN Ceramic Fibers Containing Amorphous Silicon Nitride

Boron nitride (BN) ceramic fibers containing amounts of silicon nitride (Si₃N₄) were prepared using hybrid precursors of poly(tri(methylamino)borazine) (PBN) and polycarbosilane (PCS) via melt-spinning, curing, decarburization under NH₃ to 1000 °C and pyrolysis up to 1600 °C under N₂. The effect of Si₃N₄ contents on the microstructure of the BN/Si₃N₄ composite ceramics was investigated. Series of the BN/Si₃N₄ composite fibers containing various amounts of Si₃N₄ from 5 wt% to 25 wt% were fabricated. It was found that the crystallization of Si₃N₄ could be totally restrained when its content was below 25 wt% in the BN/Si₃N₄ composite ceramics at 1600 °C, and the amorphous BN/Si₃N₄ composite ceramic could be obtained with a certain ratio. The mean tensile strength and Young's modulus of the composite fibers correlated positively with the Si₃N₄ mass content, while an obvious BN (shell)/Si₃N₄ (core) was formed only when the Si₃N₄ content reached 25 wt%.