Multilayer reduced graphene oxide (mrGO) was chemically modified by electroless plating of copper on surface to form mrGO-Cu. The scanning electron microscope (SEM) and transmission electron microscope (TEM) analysis revealed that nano-Cu particles were uniformly dispersed on the surface of mrGO. The mrGO-Cu powders were further utilized as reinforcements for aluminum (Al) matrix and the mrGO-Cu/Al composite was successfully fabricated through clad rolling of milled powder. The tribological properties of the mrGO-Cu/Al composites were explored. The tribological results show that the mrGO-Cu could reduce the friction coefficient and wear loss of mrGO-Cu/Al composites, since the mrGO-Cu participated in lubricating processes due to the formation of a transfer layer on the contact surface. Furthermore, it is found that the composition of mrGO-Cu could significantly influence the tribological properties of the mrGO-Cu/Al composites. The composites with 4% of mrGO-Cu for composites exhibited the best tribological behavior, which transformed from adhesive wear to abrasive wear, due to the formation of a graphite lubricating film.
Keywords: aluminum matrix composites; multilayer reduced graphene oxide; tribological properties.