A novel micro-cellular polymer with a well-defined and uniform micro-architecture has been developed as a three-dimensional support matrix for in vitro tissue engineering applications. This material is manufactured through a high internal phase emulsion (HIPE) polymerization route and may be modified with hydroxyapatite. The generic form of the support is known as PolyHIPE Polymer (PHP). By changing the chemical composition of the emulsion and the processing conditions, the pore size can be altered from sub-micron range to a few hundred microns and the porosity varied from 70% to 97%. Our work has investigated the use of this micro-porous polymer as a biomaterial to support the growth of osteoblasts, the bone forming cells in vitro. Three groups of polymers were used that had pore sizes of 40, 60 and 100 microm. Results demonstrated in vitro cell-polymer compatibility, with osteoblasts forming multicellular layers on the polymer surface and also migrating to a maximum depth of 1.4mm inside the scaffold after 35 days in culture. PHP was also able to support the differentiation of osteoblasts and the production of a bone-like matrix. The effect of modifying the polymer with hydroxyapatite was also studied and showed that there was a significant increase in osteoblast numbers penetrating into the polymer. There were few differences, between the pore sizes studied, on the overall penetration of osteoblasts into the polymer but the rate of movement into 100 microm PHP was significantly higher compared to the other sizes investigated. This study shows that osteoblasts seeded onto PHP demonstrate cellular attachment, proliferation and ingrowth leading to the support of an osteoblastic phenotype. Therefore this highly porous scaffold has a potential for bone tissue engineering.