Purpose: Ultraviolet (UV)-mediated photofunctionalization technology is intended to enhance the osseointegration capability of titanium implants. There are concerns about orthodontic anchor screws loosening under immediate loading protocols in adolescent orthodontic treatment. The purpose of this in vivo study was to evaluate the effects of photofunctionalization on the intrabony stability of orthodontic titanium anchor screws and bone-anchor screw contact under immediate loading in growing rats.
Materials and methods: Custom-made titanium anchor screws (1.4 mm in diameter and 4.0 mm in length) with or without photofunctionalization pretreatment were placed on the proximal epiphysis of the tibial bone in 6-week-old male Sprague-Dawley rats and were loaded immediately after placement. After 2 weeks of loading, the stability of the anchor screws was evaluated using a Periotest device, and the bone-anchor screw contact ratio (BSC) was assessed by a histomorphometric analysis using field-emission scanning electron microscopy.
Results: In the unloaded group, Periotest values (PTVs) were ~25 for UV-untreated screws and 13 for UVtreated screws (P < .01), while in the immediate-loading group, PTVs were 28 for UV-untreated screws and 16 for UV-treated screws (P < .05). Significantly less screw mobility was observed in both UV-treated groups regardless of the loading protocol. The BSC was increased ~1.8 fold for UV-treated screws, compared with UV-untreated screws, regardless of the loading protocol.
Conclusion: Photofunctionalization enhanced the intrabony stability of orthodontic anchor screws under immediate loading in growing rats by increasing bone-anchor screw contact.